(a) Class I-L. Piping systems designated to operate at temperatures below 0 [deg]F. and pressures above 150 pounds per square inch gage shall be of Class I-L. Exceptions to this rule may be found in the individual requirements for specific commodities in subchapters D, I, and O of this chapter. The following requirements for Class I-L piping systems shall be satisfied:
(1) Materials. All materials used in low temperature piping systems shall be selected from among those specifications listed in Table 56.50-105 and shall satisfy all of the requirements of the specifications, except that:
(i) The minimum service temperature as defined in Sec. 54.25-10(a)(2) of this subchapter shall not be colder than that shown in Table 56.50-105; and
(ii) The material shall be tested for low temperature toughness using the Charpy V-notch specimen of ASTM E 23 (incorporated by reference, see Sec. 56.01-2), ``Notched Bar Impact Testing of Metallic Materials'', Type A, Figure 4. The toughness testing requirements of subpart 54.05 of this subchapter shall be satisfied for each particular product form. Charpy V-notch tests shall be conducted at temperatures not warmer than 10 [deg]F. below the minimum service temperature of the design, except that for service temperatures of -320 [deg]F. and below, the impact test may be conducted at the service temperature. The minimum average energy shall not be less than that shown in Table 56.50-105. In the case of steels conforming to the specifications of Table 54.25-20(a) of this subchapter the minimum lateral expansion shall not be less than that required in Sec. 54.25-20 of this subchapter. The minimum energy permitted for a single specimen and the minimum subsize energies shall be those obtained by multiplying the average energy shown in Table 56.50-105 by the applicable fraction shown in Table 56.50-105(a).
Table 56.50-105(a)--Charpy V-Notch Energy Multiplying Factors------------------------------------------------------------------------
Factor for Factor for
minimum minimum
energy, energy
Charpy V-notch specimen size \1\ average of single
3 specimens specimen
\1\ \1\------------------------------------------------------------------------10 x 10 mm.................................... 1 2/310 x 7.5 mm................................... 5/6 5/910 x 5.0 mm................................... 2/3 4/910 x 2.5 mm................................... 1/2 1/3------------------------------------------------------------------------\1\ Straight line interpolation for intermediate values is permitted.
(iii) Steels equivalent to those listed in Table 56.50-105 of this part, but not produced according to a particular ASTM specification, may be used only with the prior consent of the Marine Safety Center. Steels differing in chemical composition, mechanical properties or heat treatments from those specified may be specially approved by the Marine Safety Center. Similarly, aluminum alloys and other nonferrous materials not covered in Table 56.50-105 of this part may be specifically approved by the Marine Safety Center for service at any low temperature. There are restrictions on the use of certain materials in this part and in subchapter O of this chapter.
(2) Piping weldments. Piping weldments shall be fabricated to satisfy the requirements of Sec. 57.03-1(b) of this subchapter in addition to subpart 56.70. Toughness testing of production weldments for low temperature piping systems and assemblies is not required.
(3) Postweld heat treatment. All piping weldments shall be postweld heat treated for stress relief in accordance with the procedures of subpart 56.85. The only exceptions to this requirement are for materials which do not require postweld heat treatment as shown in Table 56.85-10. Relief from postweld heat treatment shall not be dependent upon pipe thickness or weld joint type.
(4) Nonacceptable joints. Single welded butt joints with backing ring left in place, socket welds, slip-on flanges, pipe joining sleeves, and threaded joints shall not be used, except in small diameter instrument lines.
(5) Other requirements. All other requirements of this part for Class I piping apply to Class I-L piping. Pressure testing must comply with subpart 56.97 of this part, and nondestructive testing of circumferentially welded joints must comply with Sec. 56.95-10. Seamless tubular products must be used except that, when the service pressure does not exceed 1724 KPa (250 psi), the Commanding Officer, Marine Safety Center, may give special consideration to appropriate grades of piping and tubing that are welded without the addition of filler metal in the root pass. Each production procedure and quality-control program for welded products must be acceptable to the Officer in Charge, Marine Inspection.
(b) Class II-L. Piping systems designed to operate at temperatures below 0 [deg]F. and pressures not higher than 150 pounds per square inch gage shall be of Class II-L. Exceptions to this rule may be found in the individual requirements for specific commodities in subchapter D (Tank Vessels) and I (Cargo and Miscellaneous Vessels) of this chapter. The following requirements for Class II-L piping systems shall be satisfied:
(1) Materials must be the same as those required by paragraph (a)(1) of this section except that pipe and tubing of appropriate grades welded without the addition of a filler metal may be used. The Commandant may give special consideration to tubular products welded with the addition of filler metal.
(2) Piping weldments shall be fabricated to satisfy the requirements of Sec. 57.03-1(b) of this subchapter in addition to subpart 56.70. Toughness testing of production weldments for low temperature piping systems and assemblies is not required.
(3) All piping weldments shall be postweld heat treated for stress relief in accordance with the procedures of subpart 56.85. The only exceptions to this requirement are for materials which do not require postweld heat treatment as shown in Table 56.85-10 and for socket weld joints and slip-on flange weld attachments where the weld thickness does not exceed that exempted by this table. Otherwise, relief from post-weld heat treatment shall not be dependent upon pipe thickness or weld joint type.
(4) Socket welds in nominal sizes above 3 inches, slip-on flanges in nominal sizes above 4 inches, and threaded joints in sizes above 1 inch shall not be used.
(5) Pressure testing must comply with subpart 56.97, and nondestructive testing of welded joints must comply with Sec. 56.95-10.
(6) All other requirements contained in this part for Class II piping shall be applicable to Class II-L systems, except that Sec. 56.70-15(b)(3)(iv) shall not apply.
Table 56.50-105--Acceptable Materials and Toughness Test Criteria \2\----------------------------------------------------------------------------------------------------------------
ASTM specification Minimum service Minimum avg Charpy
Product form \3\ Grade \4\ temperature V notch energy----------------------------------------------------------------------------------------------------------------Pipe............................ 1................. -30 [deg]F........ 20 ft. lb.
3................. -150 [deg]F....... 25 ft. lb.Tube (carbon and low A-333 and 4 (A-333 only).... -100 [deg]F....... 25 ft. lb.
alloy steels). A-334............. 6................. -30 [deg]F........ 20 ft. lb.
7................. -100 [deg]F....... 25 ft. lb.
8................. -320 [deg]F....... Refer to Sec.
54.25-20 of this
subchapter.Pipe (Austenitic stainless A-312............. All Grades........ No limit.......... Austenitic
steel). stainless steel
piping need be
impact tested
only when
toughness tests
are specified in
subpart 54.25 of
this subchapter
for plating of
the same alloy
designation. When
such toughness
tests are
required, the
minimum average
energy is 25 ft.
lb.Wrought welding fittings WPL1.............. -30 [deg]F........ 20 ft. lb.
(carbon and low alloy A-420............. WPL3.............. -150 [deg]F....... 25 ft. lb.
steels). WPL4.............. -100 [deg]F....... 25 ft. lb.Forged or rolled flanges, LF1............... -30 [deg]F........ 20 ft. lb.
forged fittings, valves A-350 \1\......... LF2............... -30 [deg]F........ 20 ft. lb.
and pressure parts LF3............... -150 [deg]F....... 25 ft. lb.
(carbon and low alloy LF4............... -100 [deg]F....... 25 ft. lb.
steels).Forged or rolled flanges, forged A-182............. Austenitic grades No limit.......... These products
fittings, valves and pressure only (304, 304H, need be impact
parts (high alloy steels). 304L, 310, 316, tested only when
316H, 316L, 321, toughness tests
321H, 347, 347H, are specified in
348, 348H). subpart 54.25 of
this subchapter
for plating of
the same alloy
designation. When
such toughness
tests are
required, the
minimum average
energy is 25 ft.
lb.Forged flanges, fittings, A-522............. 9% Ni............. -320 [deg]F....... Refer to Sec.
54.25-20 of
and valves (9% nickel). this subchapter.Castings for valves and LCB............... -30 [deg]F........ 20 ft. lb.
pressure parts (carbon A-352\1\.......... LC1............... -50 [deg]F........ 20 ft. lb.
and low alloy steels). LC2............... -100 [deg]F....... 25 ft. lb.
LC3............... -150 [deg]F....... 25 ft. lb.Castings for valves and pressure A-351............. Austenitic grades No limit, except - No toughness
parts (high alloy steel). CF3, CF3A, CF8, 325 [deg]F for testing required
CF8A, CF3M, CF8M, grades CF8C and except for
CF8C, CK20 only. CK20. service
temperatures
colder than -425
[deg]F for grades
CF3, CF3A, CF8,
CF8A, CF3M, and
CF8M. 25 ft. lb.
average must be
attained in these
tests.Bolting......................... A-320............. L7, L9, L10, L43.. -150 [deg]F....... 20 ft. lb.
B8D, B8T, B8F, B8M -325 [deg]F....... No test required.
2B8, B8C.......... No limit.......... No test required,
except for
service
temperatures
colder than -425
[deg]F. In such
case the minimum
average energy is
25 ft. lb.
4................. -150 [deg]F....... 20 ft. lb.Nuts, bolting................... A-194............. 8T, 8F............ -325 [deg]F....... No test required.
8, 8C............. No limit.......... Same requirement
as comparable
grades (B8, B8C)
of bolting listed
above.----------------------------------------------------------------------------------------------------------------\1\ Quench and temper heat treatment may be permitted when specifically authorized by the Commandant. In those
cases the minimum average Charpy V-notch energy shall be specially designated by the Commandant.\2\ Other material specifications for product forms acceptable under part 54 for use at low temperatures may
also be used for piping systems provided the applicable toughness requirements of this Table are also met.\3\ Any repair method must be acceptable to the Commandant CG-ENG, and welding repairs as well as fabrication
welding must be in accordance with part 57 of this chapter.\4\ The acceptability of several alloys for low temperature service is not intended to suggest acceptable
resistance to marine corrosion. The selection of alloys for any particular shipboard location must take
corrosion resistance into account and be approved by the Marine Safety Center.
Note: The ASTM standards listed in table 56.50-105 are incorporated by reference; see 46 CFR 56.01-2. [CGFR 68-82, 33 FR 18843, Dec. 18, 1968, as amended by CGFR 72-59R, 37 FR 6189, 6190, Mar. 25, 1972; CGD 73-254, 40 FR 40165, Sept. 2, 1975; CG 79-108, 43 FR 46545, Oct. 10, 1978; CGD 74-289, 44 FR 26008, May 3, 1979; CGD 77-140, 54 FR 40611, Oct. 2, 1989; CGD 83-043, 60 FR 24775, May 10, 1995; USCG-2000-7790, 65 FR 58460, Sept. 29, 2000; USCG-2003-16630, 73 FR 65178, Oct. 31, 2008; USCG-2009-0702, 74 FR 49228, Sept. 25, 2009; USCG-2012-0832, 77 FR 59777, Oct. 1, 2012]